EC number: 215-148-3 | CAS number: 1306-24-7
Auto flammability
Administrative data
Link to relevant study record(s)
- Endpoint:
- relative self-ignition temperature (solids)
- Type of information:
- experimental study
- Adequacy of study:
- key study
- Study period:
- 15 November 2017 to 17 November 2017
- Reliability:
- 1 (reliable without restriction)
- Rationale for reliability incl. deficiencies:
- guideline study
- Qualifier:
- according to guideline
- Guideline:
- EU Method A.16 (Relative Self-Ignition Temperature for Solids)
- Deviations:
- no
- GLP compliance:
- yes (incl. QA statement)
- Key result
- Relative self-ignition temperature:
- > 400 °C
- Remarks on result:
- no self ignition observed under the test conditions
- Conclusions:
- Three replicate tests were performed. No relative self-ignition temperature of Cadmium selenide was observed up to 400°C.
- Executive summary:
The purpose of this test was to provide preliminary information on the auto-flammability of solid substance at elevated temperatures. A specific amount of the test substance was placed in a wire-mesh cube into an oven at room temperature; the temperature difference/time curve of the sample of test item was recorded while the temperature of the oven is increased to 400°C at a rate of 0.5°C/min. For the purpose of this test, the temperature of the oven at which the sample temperature reaches 400°C by self-heating is called the self-ignition temperature.
Three replicate tests were performed. No relative self-ignition temperature of Cadmium selenide was observed up to 400°C.
The test item was not auto-flammable under the conditions of the test.
Reference
Description of key information
Key value determined in a GLP accredited laboratory study using relative self-ignition test, in accordance with EU Method A.16 (Relative Self-Ignition Temperature for Solids)
Key value for chemical safety assessment
- Autoflammability / Self-ignition temperature at 101 325 Pa:
- 400 °C
Additional information
The purpose of this test was to provide preliminary information on the auto-flammability of solid substance at elevated temperatures in accordance with EU Method A.16 (Relative Self-Ignition Temperature for Solids).
A specific amount of the test substance was placed in a wire-mesh cube into an oven at room temperature; the temperature difference/time curve of the sample of test item was recorded while the temperature of the oven is increased to 400°C at a rate of 0.5°C/min. For the purpose of this test, the temperature of the oven at which the sample temperature reaches 400°C by self-heating is called the self-ignition temperature.
Three replicate tests were performed. No relative self-ignition temperature of Cadmium selenide was observed up to 400°C.
The test item was not auto-flammable under the conditions of the test.
Information on Registered Substances comes from registration dossiers which have been assigned a registration number. The assignment of a registration number does however not guarantee that the information in the dossier is correct or that the dossier is compliant with Regulation (EC) No 1907/2006 (the REACH Regulation). This information has not been reviewed or verified by the Agency or any other authority. The content is subject to change without prior notice.